Abstract
A new layer transfer technique which comprised double bonding and a step annealing process was utilized to transfer the GaN epilayer from a sapphire substrate to a Mo substrate. Combined with the application of the thermal-stable bonding medium, the resulting two-inch-diameter GaN template showed extremely good stability under high temperature and low stress state. Moreover, no cracks and winkles were observed. The transferred GaN template was suitable for homogeneous epitaxial, thus could be used for the direct fabrication of vertical LED chips as well as power electron devices. It has been confirmed that the double bonding and step annealing technique together with the thermal-stable bonding layer could significantly improve the bonding strength and stress relief, finally enhancing the thermal stability of the transferred GaN template.
Keywords:GaN template
If you need more information about GaN template, please visit our website: www.qualitymaterial.net, and send us email at send us email at angel.ye@powerwaywafer.com or powerwaymaterial@gmail.com.
1 comment:
I am very grateful that I got some useful knowledge from this post. Thank you so much for posting it. Keep it up. Plastic Extrusion Manufacturer
Post a Comment