Fabrication of extremely thermal-stable GaN template on Mo substrate using double bonding and step annealing process*

A new layer transfer technique which comprised double bonding and a step annealing process was utilized to transfer the GaN epilayer from a sapphire substrate to a Mo substrate. Combined with the application of the thermal-stable bonding medium, the resulting two-inch-diameter GaN template showed extremely good stability under high temperature and low stress state. Moreover, no cracks and winkles were observed. The transferred GaN template was suitable for homogeneous epitaxial, thus could be used for the direct fabrication of vertical LED chips as well as power electron devices. It has been confirmed that the double bonding and step annealing technique together with the thermal-stable bonding layer could significantly improve the bonding strength and stress relief, finally enhancing the thermal stability of the transferred GaN template.

Source:IOPscience
For more information, please visit our website: www.semiconductorwafers.net,
send us email at sales@powerwaywafer.com and powerwaymaterial@gmail.com

3 comments:

legacymarbleandgranite said...

Mostly I do not comment on any post, but your blog has lots of knowledge. it's forcing me to do this. it has really amazing content please share more information with us.Custom Fabrication

Dwayne said...

You are really awesome as the post you have shared here is really interesting and informative also. Thanks for posting it. Keep it up. 230 V Industrial Electric Motors For Sale

glassline said...

I just stumbled upon your blog and wanted to mention that I even have enjoyed reading your blog posts. I hope you post again soon. Big thanks for the useful info. Glass Fabrication Equipment